Influence of laser beam brightness during laser surface treatment of ZrO2 engineering ceramics

Shukla, Pratik and Lawrence, Jonathan and Paul, Anish (2012) Influence of laser beam brightness during laser surface treatment of ZrO2 engineering ceramics. Lasers in Engineering, 22 (3/4). pp. 151-173. ISSN 0898-1507

Full text not available from this repository.

Item Type:Article
Item Status:Live Archive

Abstract

A comparative study between fibre and Nd:YAG (neodymium, yttrium, aluminium, garnet) laser surface treatment on a cold isostatic pressed (CIP) ZrO 2 engineering ceramic was conducted to investigate the individual differences of laser brightness (radiance) produced by the two laser sources. The effects of brightness exhibited by the two lasers were investigated in respect to the change in the hardness, dimensional size of the laser irradiated zones and the microstructure of the ZrO 2 engineering ceramic. The results showed that the hardness of the ZrO 2 engineering ceramic was reduced by 36% for the Nd:YAG laser in comparison to the as-received surface. However, only 4% reduction in the surface hardness was found from employing the fibre laser surface treatment which was not significant as much as the results of the Nd:YAG laser irradiation. The change in hardness occurred due to softening of the laser irradiated surface of the ZrO 2 with a changed composition which was softer than the laser unaffected surface. The dimensional size of the fibre laser irradiated track was also found to produce broader surface profiles in comparison to that of the Nd:YAG laser. The fibre laser irradiated surface track was 32% larger in width and 51.5% longer in depth of penetration in comparison to that of the Nd:YAG laser. Change in microstructure of the ZrO 2 engineering ceramic irradiated by both lasers was found as opposed to the ground and polished untreated surface. The fibre laser affected the grain morphology to a greater extent in comparison to that of the Nd:YAG laser irradiation. The physical and micro-structural effects from applying the two laser types to the ZrO 2 engineering ceramic differed as deep penetration and broader laser irradiated track as well as larger grains were produced by the fibre laser, despite using identical laser processing parameters such as spot size, power density, traverse speed, gas flow rate, wavelength and the Gaussian beam profile. This occurred due to the high brightness exhibited by the fibre laser irradiation which generated larger power per unit area which in turn induced into the ZrO 2 engineering ceramic and resulted to producing high processing temperature, larger fibre laser-ceramic-interaction zone and melt-pool at the laser-ZrO 2 interface in comparison to that of the Nd:YAG laser which intrinsically resulted to a change in physical attributes of the ceramic. © 2011 Old City Publishing, Inc.

Keywords:Lasers, Brightness, Zirconia Ceramics
Subjects:F Physical Sciences > F200 Materials Science
J Technologies > J310 Ceramics
F Physical Sciences > F361 Laser Physics
Divisions:College of Science > School of Engineering
Related URLs:
ID Code:9255
Deposited On:01 May 2013 17:19

Repository Staff Only: item control page